Hydroxy proply Methyl Cellulose
CheSilo MPC 75M can be used in tile adhesive.
Viscosity:34000-38000cps(20 â„ƒ ,Brookfield RVT,2% solution )
Methoxyl Content,% :25.0~30.0
Hydroxypropyloxy Content,% :4.0~12.0
Package:25kg/bag,600kg/Pallet,12tons with 20pallets in 20'fcl.
This is Heaven Zhu from Chemix Specialty Chemical Co.,ltd(C.S.C.). wechat:18217263323
C.S.C is one of main suppliers for mortar, coating additives and specialty chemicals in China. At the beginning of establishing in 2010, it was a representative for Chinese well-known special chemicals manufacturers.
CheSilo TM Hydroxy Propyl Methyl Cellulose
Molecular Formula: [C6H7O2ï¼ˆOHï¼‰x-m-nï¼ˆOCH3ï¼‰mï¼ˆOCH2CHï¼ˆOHï¼‰CH3ï¼‰n]x
Wherein, R stands for –H, -CH3 or –CH2CHOHCH3 and x for degree of polymerization
CheSilo Hydroxy Propyl Methyl Cellulose(abb.CheSilo HPMC) is a non-ionic, water soluble cellulose ether.
It is widely used as as thickener, protective colloid, stabilizer,suspending aids and water-retention agents in many industrial applications.
1.Appearanceï¼ša white to light yellow powder or granular product.
2.Solubilityï¼šCheSilo CheSilo HPMC is nearly insoluble in anhydrous ethanol, ethyl ether and acetone.
It is swelled in cold water to form a transparent or a slight cloudy solution.
It can be dissolved into some organic solvents and also in water-organic solvent mixed solvents.
3.Fineness(Graininess)ï¼šThe oversize product above 100 mesh should not exceed 5.0%.
4.With reduction of methoxyl groups content, CheSilo CheSilo HPMC is increased in gelling temperature and decreased in water solubility
and surface activity.
1.Resistance to salting outï¼šCheSilo CheSilo HPMC is a nonionic cellulose ether and it is not a polyelectrolyte.
The aqueous solution of CheSilo CheSilo HPMC is comparatively stable even in.
2.the presence of metal salts or organic electrolytes. However, when the concentration of electrolytes exceeds a certain limit,
gelation and precipitation may result.
3.Surface activityï¼šAn aqueous solution of CheSilo CheSilo HPMC has a high surface activity and functions as
a protective colloid agent, emulsion stabilizer and dispersant.
4.Thermal gelationï¼šAn aqueous solution of CheSilo CheSilo HPMC will gel or precipitate when heated to a certain temperature,
but it reverts to the original solution state on subsequent cooling. The temperature at which gelation or precipitation occur depends on the
type of CheSilo CheSilo HPMC, its concentration and the rate of heating.
5.pH stabilityï¼šThe viscosity of an aqueous solution of CheSilo CheSilo HPMC is hardly affected by acid or alkali,
and the product can develop an original viscosity in the range of 3.0~11.0. Therefore,
the solution viscosity tends to keep stable during prolonged storage.
6.Water retentionï¼šCheSilo CheSilo HPMC is a high effective water retention agent.
Its pharmaceutical grade product can be widely used in food, cosmetics and many other fields.
grease. In food application, this property is often utilized for water retention and oil adsorption.
1) Good performance to thermal shock, corrosion, erosion and abrasion resistance.
2) High refractoriness and excellent mechanical strength.
3) Both intermittently and continuously working mode are acceptable, reducing lining cracks.
4) Longer and stable life cycle to reach high efficiency.
5) Suit for all kinds of metal types, reduce residue and porosity of the products.
6) Labor and cost saving by convenient installation and maintenance.
Chemical property: Neutral
Main contents: Fused corundum
Density: >3.18 g/cm3
Linear changing rate: +0.02%
Grain size: 0-8 mm
Refractoriness: 2300° C
Compressive strength: 1500° C× 2h> 62(MPa
Thermal shock resistance: Excellent
Installation mode: Dry vibration
Suggested Working Mode: Intermittently or continuously
Suggested furnace size: ≤ 20metric tons
Storage life: 6 month in dry condition
Application: Suitable for all kinds metal types.
1)High refractoriness and good performance to slag resistance
2)Convenient installation and low-cost maintenance
3)No need to heat or add water
4)Free from the size of the furnace
5)Prolong the campaign length
Main Contents: MGO-Fe2O3-CaO
Combination Mode: Ceramic bond
Burned Compressive Strength: 1200C× 3h>12MPa
Burned linear Changing Rate: 1200C× 3h: 0.4%
1600C× 3h: 2.8%
Construction Thickness: ≥ 500mm
Construction Dosage: 3t/M3
Application: Lower ring and wall of induction furnace.
High Strength, Abrasion Resistant and Corrosion Resistant Repair Mastic-----HQRM Series
Huaqian®& lt; /sup> Epoxy Repair Mastic
·< /span>High Bond Strength
·< /span>High Strength
·< /span>Abrasion Resistant
·< /span>Corrosion Resistant
·< /span>Pull-out Strength: 34.7Mpa
·< /span>Compressive Strength: 72.4Mpa
·< /span>Flexural Strength: 47.2Mpa
·< /span>Modulus of Tensile Elasticity: 3.55×103Mpa
·< /span>Unit Weight: about 1500kg/m3
·< /span>Apply to concrete for seepage-proof, anti-Carbonization protection, micro-cracks sealing and appearance beautifying
· Repairing surface defects of high-speed railway compartment beams and track boards
· Repairing light abrasion of scoured concrete surfaces, like surfaces without cream, fine aggregate exposure, harsh handling, etc.
·< /span>Long-term standing will cause precipitation and segregation, shake up before using.
·< /span>Recommended mechanical mixing, and evenly mixing material A and material B at the ratio of 1:4.
Application methods: blade coating
Working Time ≥30min
Application Temperature: Over 5℃ is appropriate and avoid construction in rainy and frozen conditions.
Storage: ventilated cool conditions over 5℃without direct sunlight
Shelf life: 12months when sealed
< /b>Packaging: Material A: 5kg/barrel, Material B: 15kg/barrel
Multi-functional Construction Adhesive Powder-----HQGA Series
Huaqian® Adhesive Powder 108
Organic Polymer Powder, High Solubility
Small Volume, Long Shelf Life, Convenient in storage and transport
Easy to use, Directly dissolve in water to use and effectively reduce the waste in worksite
Ÿ Directly mix with the cement grout at the given ratio, or dissolve 250g HQGA-108 in 50L water.
Mixing Ratio for Reference
·For the Preparation of Adhesive Mortar：
Apply to paste ceramic tiles, vitrified tiles, split tiles, cultural stones, etc.
Mixing Ratio: “HQGA-108 : Water: Cement: Sand=250g: 50kg: 100kg: 150～200kg”
·For the Preparation of Plastering Mortar：
Leveling and Plastering the base course of brick walls, concrete walls, masonry walls, etc.
Mixing Ratio: “HQGA-108: Water：Cement：Sand=250g：50kg：50～100kg：150kg～200kg”
·Base Course Galling：
Mixing Ratio: “HQGA-108: Water: Cement=250g: 50kg: 150～200kg”
·On the Preparation of Water Resistant Putty：
Apply to bottom leveling and base course treatment.
Mixing Ratio: “HQGA-108: Water: Cement: Limestone Powder＝250g: 50kg: 50～100kg: 100～150kg”
Storage: ventilated dry conditions, waterproof, damp proof
Shelf life: 12months
Packaging : 25kg/bag
Package:25kg/50kg per bag